NYLON PA11
NYLON PA11
PA11 offers heat resistance, toughness and strength for functional applications. It requires no support structures during printing and suits prototypes with highly complex geometries.
| Parameter | Method | Result |
|---|---|---|
| Heat deflection (0.46 MPa) | GB/T 1634.2-2004 | 151.1℃ |
| Heat deflection (1.82 MPa) | GB/T 1634.2-2004 | 51℃ |
| Melting point | GB/T 19466.1-2004 | 201 ℃ |
| Tensile strength | GB/T 1040.2-2006 | 48 MPa |
| Tensile modulus | GB/T 1040.2-2006 | 1483 MPa |
| Elongation at break | GB/T 1040.2-2006 | 56% |
| Flexural strength | GB/T 9341-2008 | 59 MPa |
| Flexural modulus | GB/T 9341-2008 | 1470 MPa |
| Notched impact strength | GB/T 1843-2008 | 26 KJ/㎡ |
| Unnotched impact strength | N/A | N/A |
NYLON PA12 GLASS-FILLED LIGHT GRAY
NYLON PA12 GLASS-FILLED LIGHT GRAY
Light-grey glass-filled PA12 offers heat resistance, dimensional stability, toughness, insulation, corrosion resistance and high mechanical strength. Glass fibres improve heat deflection temperature and strength compared with conventional nylon. We recommend it for structural checks of prototypes such as automotive parts, household appliances and electromechanical devices.
| Parameter | Method | Result |
|---|---|---|
| Heat deflection (0.46 MPa) | GB/T 1634.2-2004 | 153.1 ℃ |
| Heat deflection (1.82 MPa) | GB/T 1634.2-2004 | 69 ℃ |
| Melting point | GB/T 19466.1-2004 | 184.5 ℃ |
| Tensile strength | GB/T 1040.2-2006 | 45 MPa |
| Tensile modulus | GB/T 1040.2-2006 | 2600 MPa |
| Elongation at break | GB/T 1040.2-2006 | 6.7% |
| Flexural strength | GB/T 9341-2008 | 60 MPa |
| Flexural modulus | GB/T 9341-2008 | 2100 MPa |
| Notched impact strength | GB/T 1843-2008 | 6.1 kJ/m² |
| Unnotched impact strength | GB/T 1843-2008 | 31.2 kJ/m² |
| Colour | Light grey |
NYLON PA12 GRAY BLACK
NYLON PA12 GRAY BLACK
Grey-black PA12 offers heat resistance, toughness and strength for functional applications. It needs no support structures when printing and suits prototypes with highly complex geometries.
| Parameter | Method | Result |
|---|---|---|
| Heat deflection (0.46 MPa) | GB/T 1634.2-2004 | 146.1 ℃ |
| Heat deflection (1.82 MPa) | GB/T 1634.2-2004 | 73.1 ℃ |
| Melting point | GB/T 19466.1-2004 | 184.5 ℃ |
| Tensile strength | GB/T 1040.2-2006 | 47 MPa |
| Tensile modulus | GB/T 1040.2-2006 | 1951 MPa |
| Elongation at break | GB/T 1040.2-2006 | 19% |
| Flexural strength | GB/T 9341-2008 | 40.1 MPa |
| Flexural modulus | GB/T 9341-2008 | 1053.7 MPa |
| Notched impact strength | GB/T 1843-2008 | 8.6 kJ/m² |
| Unnotched impact strength | GB/T 1843-2008 | 23.1 kJ/m² |
| Colour | Grey-black |
NYLON PA12 WHITE
NYLON PA12 WHITE
White PA12 offers high heat resistance, toughness and strength. It suits functional parts and prototypes intended to behave like the final product. It needs no printing supports and allows highly complex structures. Nylon parts naturally have a grainy surface; together with our partners, we offer 3D Plus services such as vapour smoothing when a smoother finish is required.
| Parameter | Method | Result |
|---|---|---|
| Heat deflection (0.46 MPa) | GB/T 1634.2-2004 | 148.2℃ |
| Heat deflection (1.82 MPa) | GB/T 1634.2-2004 | 84.5℃ |
| Melting point | GB/T 19466.1-2004 | 185 ℃ |
| Tensile strength | GB/T 1040.2-2006 | 45 MPa |
| Tensile modulus | GB/T 1040.2-2006 | 1600 MPa |
| Elongation at break | GB/T 1040.2-2006 | 38% |
| Flexural strength | GB/T 9341-2008 | 46.1 MPa |
| Flexural modulus | GB/T 9341-2008 | 1297 MPa |
| Notched impact strength | GB/T 1843-2008 | 4.8 KJ/㎡ |
| Unnotched impact strength | GB/T 1843-2008 | 13.3 KJ/㎡ |
| Colour | White |
These values come from our existing material overview and are for guidance. Suitability and binding requirements are clarified with your enquiry.
The right material.
Compare materials by technology and select them together.
The right finish.
These options depend on the material and part specifications.
We confirm suitability based on the material, geometry and requirements.