MJF materials.
Suited to the task.
PA11 and PA12 for precise, functional plastic parts. Find available variants and their material properties here.
No matching material found. Try a different search term.
NYLON PA11
NYLON PA11
Nylon PA11 was developed specifically for HP’s MJF printing technology. Its high dimensional accuracy highlights details and enables precise small holes, thin walls, shafts, robust structural parts, complex components and lattice structures.
| Parameter | Method | Result |
|---|---|---|
| Heat deflection (0.46 MPa) | ASTM D648 Test Method A | 185℃ |
| Heat deflection (1.82 MPa) | ASTM D648 Test Method A | 54℃ |
| Melting point | ASTM D3418 | 202 ℃ |
| Tensile strength | ASTM D638 | 52 MPa |
| Tensile modulus | ASTM D638 | 1800 MPa |
| Elongation at break | ASTM D638 | 50% |
| Flexural strength | ASTM D790 | 70 MPa |
| Flexural modulus | ASTM D790 | 1800 MPa |
| Notched impact strength | ASTM D256 Test Method A | 5 KJ/㎡ |
NYLON PA 12 BLACK
NYLON PA 12 BLACK
Black nylon PA12 was developed specifically for HP’s MJF printing technology. Its high dimensional accuracy highlights details and enables precise small holes, thin walls, shafts, robust structural parts, complex components and lattice structures.
| Parameter | Method | Result |
|---|---|---|
| Heat deflection (0.46 MPa) | ASTM D648 Test Method A | 145℃ |
| Heat deflection (1.82 MPa) | ASTM D648 Test Method A | 82℃ |
| Melting point | ASTM D3418 | 183 ℃ |
| Tensile strength | ASTM D638 | 46 MPa |
| Tensile modulus | ASTM D638 | 1600 MPa |
| Elongation at break | ASTM D638 | 36% |
| Flexural strength | ASTM D790 | 46.3 MPa |
| Flexural modulus | ASTM D790 | 1300 MPa |
| Notched impact strength | ASTM D256 Test Method A | 3.5 KJ/㎡ |
| Colour | Dyed black |
NYLON PA12 GRAY
NYLON PA12 GRAY
Grey nylon PA12 was developed specifically for HP’s MJF printing technology. Its high dimensional accuracy highlights details and enables precise small holes, thin walls, shafts, robust structural parts, complex components and lattice structures.
| Parameter | Method | Result |
|---|---|---|
| Heat deflection (0.46 MPa) | ASTM D648 Test Method A | 145℃ |
| Heat deflection (1.82 MPa) | ASTM D648 Test Method A | 82℃ |
| Melting point | ASTM D3418 | 183 ℃ |
| Tensile strength | ASTM D638 | 46 MPa |
| Tensile modulus | ASTM D638 | 1600 MPa |
| Elongation at break | ASTM D638 | 36% |
| Flexural strength | ASTM D790 | 46.3 MPa |
| Flexural modulus | ASTM D790 | 1300 MPa |
| Notched impact strength | ASTM D256 Test Method A | 3.5 KJ/㎡ |
These values come from our existing material overview and are for guidance. Suitability and binding requirements are clarified with your enquiry.
The right material.
Compare materials by technology and select them together.
The right finish.
These options depend on the material and part specifications.
We confirm suitability based on the material, geometry and requirements.